1. Reduced fatigue strength due to residual stress introduced during the shaft welding process
2. Reduced fatigue strength due to stress "hot spots" associated with the shaft geometry, in particular the surface roughness and the shaft shape
3. Very exceptional active corrosion in localised areas of the shaft.
To my mind item 3 exposed items 1 and 2.